Material characterization of metal induced lateral crystallization (MILC) process of amorphous silicon (a-Si) has been performed by using the spreading resistance probe (SRP) measurements. It was found that carrier mobility in boron ion implanted layer, formed in MILC region, is up to 65 % in comparison with mobility in boron ion implanted layer, formed in single crystalline silicon. It was also observed in this work that prolongation of MILC process from 1 hour to 2 hours had induced the increasing of mobility from 24 cm2/Vs to 34 cm2/Vs.