Generation of high power laser ultrasound strongly demands the advanced materials with efficient laser energy absorption, fast thermal diffusion, and large thermoelastic expansion capabilities. In this study, candle soot nanoparticles-polydimethylsiloxane (CSNPs-PDMS) composite was investigated as the functional layer for an optoacoustic transducer with high-energy conversion efficiency. The mean diameter of the collected candle soot carbon nanoparticles is about 45 nm, and the light absorption ratio at 532 nm wavelength is up to 96.24%. The prototyped CSNPs-PDMS nano-composite laser ultrasound transducer was characterized and compared with transducers using Cr-PDMS, carbon black (CB)-PDMS, and carbon nano-fiber (CNFs)-PDMS composites, respectively. Energy conversion coefficient and À6 dB frequency bandwidth of the CSNPs-PDMS composite laser ultrasound transducer were measured to be 4.41 Â 10 À3 and 21 MHz, respectively. The unprecedented laser ultrasound transduction performance using CSNPs-PDMS nano-composites is promising for a broad range of ultrasound therapy applications. V

Red phosphorus (RP) is a promising anode material for lithium-ion batteries due to its earth abundance and a high theoretical capacity of 2596 mA h g. Although RP-based anodes for lithium-ion batteries have been reported, they were all in the form of carbon-P composites, including P-graphene, P-graphite, P-carbon nanotubes (CNTs), and P-carbon black, to improve P's extremely low conductivity and large volume change during cycling process. Here, we report the large-scale synthesis of red phosphorus nanoparticles (RPNPs) with sizes ranging from 100 to 200 nm by reacting PI with ethylene glycol in the presence of cetyltrimethylammonium bromide (CTAB) in ambient environment. Unlike the insulator behavior of commercial RP (conductivity of <10 S m), the conductivity of RPNPs is between 2.62 × 10 and 1.81 × 10 S m, which is close to that of semiconductor germanium (1.02 × 10 S m), and 2 orders of magnitude higher than silicon (5.35 × 10 S m). Around 3-5 wt % of iodine-doping was found in RPNPs, which was speculated as the key to significantly improve the conductivity of RPNPs. The significantly improved conductivity of RPNPs and their uniform colloidal nanostructures enable them to be used solely as active materials for LIBs anodes. The RPNPs electrodes exhibit a high specific capacity of 1700 mA h g (0.2 C after 100 cycles, 1 C = 2000 mA g), long cycling life (∼900 mA h g after 500 cycles at 1 C), and outstanding rate capability (175 mA h g at the charge current density of 120 A g, 60 C). Moreover, as a proof-of-concept example, pouch-type full cells using RPNPs anodes and Li(NiCoMn)O (NCM-532) cathodes were assembled to show their practical uses.

Large-area conducting transparent conducting electrodes (TCEs) were prepared by a fast, scalable, and low-cost spray deposition of copper nanowire (CuNW) dispersions. Thin, long, and pure copper nanowires were obtained via the seed-mediated growth in an organic solvent-based synthesis. The mean length and diameter of nanowires are, respectively, 37.7 μm and 46 nm, corresponding to a high-mean-aspect ratio of 790. These wires were spray-deposited onto a glass substrate to form a nanowire conducting network which function as a TCE. CuNW TCEs exhibit high-transparency and high-conductivity since their relatively long lengths are advantageous in lowering in the sheet resistance. For example, a 2 × 2 cm(2) transparent nanowire electrode exhibits transmittance of T = 90% with a sheet resistance as low as 52.7 Ω sq(-1). Large-area sizes (>50 cm(2)) of CuNW TCEs were also prepared by the spray coating method and assembled as resistive touch screens that can be integrated with a variety of devices, including LED lighting array, a computer, electric motors, and audio electronic devices, showing the capability to make diverse sizes and functionalities of CuNW TCEs by the reported method.

Phosphorus (P) possesses the highest theoretical specific capacity (865 mA h g −1 ) among all the elements for potassium‐ion battery (PIB) anodes. Although Red P (RP) has intrinsic advantages over its allotropes, including low cost and nontoxicity, and simpler preparation, it is yet unknown to effectively activate it into a high‐performance PIB anode. Here, high‐performance RP PIB anodes are reported. Two important factors are found to facilitate RP react with K‐ions reversibly: i) nanoscale RP particles are dispersed evenly in a conductive carbon matrix composed of multiwall carbon nanotubes and Ketjen black that provide an efficient electrical pathway and a tough scaffold. ii) The results of X‐ray photoelectron spectroscopy spectrum and the electrochemical performance perhaps show that no P—C bond formation is beneficial to allow K‐ions to react with RP effectively. As a result, the RP/C electrodes deliver a reversible specific capacity of ≈750 mA h g −1 and exhibit a high‐rate capability (≈300 mA h g −1 at 1000 mA g −1 ). RP/C full cells using potassium manganese hexacyanoferrate as cathode show a long cycling life (680 cycles) at a current density of 1000 mA g −1 , in addition, a pouch‐type battery is built to demonstrate practical applications.

Phosphorus-rich transition metal phosphide CuP2 nanowires were synthesized with high quality and high yield (∼60%) via the supercritical fluid-liquid-solid (SFLS) growth at 410 °C and 10.2 MPa. The obtained CuP2 nanowires have a high aspect ratio and exhibit a single crystal structure of monoclinic CuP2 without any impurity phase. CuP2 nanowires have progressive improvement for semiconductors and energy storages compared with bulk CuP2. Being utilized for back-gate field effect transistor (FET) measurement, CuP2 nanowires possess a p-type behavior intrinsically with an on/off ratio larger than 10(4) and its single nanowire electrical transport property exhibits a hole mobility of 147 cm(2) V(-1) s(-1), representing the example of a CuP2 transistor. In addition, CuP2 nanowires can serve as an appealing anode material for a lithium-ion battery electrode. The discharge capacity remained at 945 mA h g(-1) after 100 cycles, showing a good capacity retention of 88% based on the first discharge capacity. Even at a high rate of 6 C, the electrode still exhibited an outstanding result with a capacity of ∼600 mA h g(-1). Ex-situ transmission electron microscopy and CV tests demonstrate that the stability of capacity retention and remarkable rate capability of the CuP2 nanowires electrode are attributed to the role of the metal phosphide conversion-type lithium storage mechanism. Finally, CuP2 nanowire anodes and LiFePO4 cathodes were assembled into pouch-type lithium batteries offering a capacity over 60 mA h. The full cell shows high capacity and stable capacity retention and can be used as an energy supply to operate electronic devices such as mobile phones and mini 4WD cars.