No abstract

No abstract

BackgroundSilver sulfadiazine (AgSD) is widely employed as an antibacterial agent for surface burn management. However, the antibacterial activity of AgSD was restrained because of the lower drug solubility and possible cytotoxicity.ObjectiveThis study aimed to formulate stable silver sulfadiazine/nanosuspensions (AgSD/NSs) with improved AgSD solubility and prepare a suitable carrier for AgSD/NS delivery. Nanotechnology was used to overcome the low drug dissolution rate of AgSD, while the new carrier loaded with AgSD/NS was assumed to decrease the possible cytotoxicity, enhance antibacterial activity, and promote wound healing.MethodsAgSD/NSs were prepared by high pressure homogenization method. Poloxamer 407-based thermoresponsive hydrogels were prepared by cold method as carriers of AgSD/NS to obtain AgSD/NS-loaded thermoresponsive hydrogel. Scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD) were used to measure the physicalchemical properties of AgSD/NSs and AgSD/NS-loaded gel. The cytotoxicity of the AgSD/NS-loaded gel was evaluated using methyl thiazolyltetrazolium assay with L929 mouse fibroblast cell lines. In vitro antibacterial activities of AgSD/NSs and AgSD/NS loaded gel were also measured.ResultsStable AgSD/NSs with an average particle size of 369 nm were formulated while 1.5% P407 was selected as a stabilizer. The optimized AgSD/NS thermoresponsive hydrogel exhibited the gelation temperature of approximately 30°C. A significant improvement in solubility was observed for AgSD nanoparticles (96.7%) compared with AgSD coarse powders (12.5%). The results of FTIR and XRD revealed that the physicochemical properties of AgSD/NS were reserved after incorporating into the hydrogel. The cell viability after incubation with AgSD/NS-loaded thermoresponsive hydrogel improved from 60.7% to 90.6% compared with incubation with AgSD/NS directly. Drug release profiles from the thermoresponsive hydrogel increased compared with the commercial AgSD cream, implying less application frequency of AgSD cream clinically. In vitro antibacterial studies manifested that AgSD nanocrystallization significantly enhanced the antibacterial activity compared with the AgSD coarse powder.ConclusionThe combination of AgSD nanosuspensions and thermoresponsive hydrogel effectively improved the AgSD antibacterial activity and decreased the cytotoxicity. This study also suggested that a poloxamer thermoresponsive hydrogel could be used as a delivery system for other nanocrystals to decrease possible nanotoxicity.

The physicochemical properties and potential hemostatic application of Wenchang kaolin and Maoming kaolin were inspected and evaluated. Chemical composition analysis, Fourier transform infrared (FTIR) spectroscopy, surface area determination, X-ray diffraction, particle size, scanning electron microscopy (SEM) observations, and zeta potential analysis were performed to quantify the physical and chemical properties of the two kaolins. The results showed that both kaolins have typical FTIR bands of kaolinite with a weight fraction for kaolinite over 90 wt%. Larger conglobate aggregates of Maoming kaolin demonstrated wider particle size distributions with two peaks at 3.17 and 35.57 μm, while the book-like Wenchang kaolin had narrow particle size distribution, with a frequent size of 5.64 μm. Furthermore, thrombelastography, the whole blood clotting tests (WBCT), plasma recalcification time (PRT) measurement, and MTT assay were performed to measure the clotting activities and biocompatibility of the two kaolins. The results showed that both kaolins could promote blood coagulation with good cytocompatibility, while Wenchang kaolin had a better procoagulant activity than Maoming kaolin. These findings demonstrated Wenchang kaolin to be a more suitable local source material for application as a hemostatic agent.

No abstract