We have studied the composition, electron emission, and optical properties of CdS single crystals covered by a surface film of adsorbed Ba atoms with thickness Θ from 0.5 to 5 monolayers (ML). It is established that, as Θ increases up to 1 ML, yield depth λ of true secondary electrons (and photoelectrons) in the emission zone exhibits significant growth, which is explained by decreasing work function of the material surface. The further increase in Θ is accompanied by a decrease in both λ and photocurrent intensity values. It is found that no significant mutual diffusion of atoms at the Ba-CdS interface takes place at room temperature. Upon heating to T = 700 K, sulfur atoms exhibit intense diffusion into the Ba film and form a surface compound of the Ba 2 S type.
Изучены состав, эмиссионные и оптические свойства монокристаллов CdS с поверхностной пленкой Ва толщиной Theta от 0.5 до 5 монослоев. Установлено, что с ростом Theta до 1 монослоя глубина зоны выхода истинно-вторичных электронов (и фотоэлектронов) λ существенно увеличивается, что объясняется уменьшением работы выхода. При дальнейшем росте Theta значения λ и интенсивность фототока уменьшаются. Показано, что при комнатной температуре не происходит заметной взаимодиффузии атомов на границе Ва-CdS. После прогрева при T=700 K происходит интенсивная диффузия S в пленку Ba и образуется соединение типа Ba2S. Ключевые слова: зона выхода электронов, адсорбция, профили распределения атомов, эмиссионная эффективность, работа выхода.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.