The design and Mg-doping profile of AlN/Al0.7Ga0.3N electron blocking heterostructures (EBH) for AlGaN multiple quantum well (MQW) light emitting diodes (LEDs) emitting below 250 nm was investigated. By inserting an AlN electron blocking layer (EBL) into the EBH, we were able to increase the quantum well emission power and significantly reduce long wavelength parasitic luminescence. Furthermore, electron leakage was suppressed by optimizing the thickness of the AlN EBL while still maintaining sufficient hole injection. Ultraviolet (UV)-C LEDs with very low parasitic luminescence (7% of total emission power) and external quantum efficiencies of 0.19% at 246 nm have been realized. This concept was applied to AlGaN MQW LEDs emitting between 235 nm and 263 nm with external quantum efficiencies ranging from 0.002% to 0.93%. After processing, we were able to demonstrate an UV-C LED emitting at 234 nm with 14.5 μW integrated optical output power and an external quantum efficiency of 0.012% at 18.2 A/cm2.

Silicon doping of AlxGa1−xN layers with high aluminum mole fractions (0.8 < x < 1) was studied. The AlGaN:Si layers were pseudomorphically grown by metalorganic vapor phase epitaxy on low defect density epitaxially laterally overgrown AlN/sapphire templates. The effects of SiH4/III ratio and aluminum content on the resistivity, the carrier concentration, and the mobility have been investigated. By variation of the SiH4/III ratio during the growth of AlxGa1−xN:Si layers, a recorded low resistivity of Al0.81Ga0.19N:Si was obtained with 0.026 Ω cm. The resistivity increases exponentially with increasing aluminum content to 3.35 Ω cm for Al0.96Ga0.04N, and the optimum SiH4/III ratio is shifted towards lower values. Hall effect measurements show that the increase of the resistivity with increasing aluminum mole fraction is mainly caused by a decrease of the carrier density. The optimized Al0.81Ga0.19N:Si exhibits a carrier concentration of 1.5 × 1019 cm−3 and a mobility of the carriers of 16.5 cm2 V−1 s−1.

The optical polarization of emission from ultraviolet (UV) light emitting diodes (LEDs) based on (0001)-oriented AlxGa1−xN multiple quantum wells (MQWs) has been studied by simulations and electroluminescence measurements. With increasing aluminum mole fraction in the quantum well x, the in-plane intensity of transverse-electric (TE) polarized light decreases relative to that of the transverse-magnetic polarized light, attributed to a reordering of the valence bands in AlxGa1−xN. Using k ⋅ p theoretical model calculations, the AlGaN MQW active region design has been optimized, yielding increased TE polarization and thus higher extraction efficiency for bottom-emitting LEDs in the deep UV spectral range. Using (i) narrow quantum wells, (ii) barriers with high aluminum mole fractions, and (iii) compressive growth on patterned aluminum nitride sapphire templates, strongly TE-polarized emission was observed at wavelengths as short as 239 nm.

No abstract

UV light emitters in the UV-B spectral range between 280 nm and 320 nm are of great interest for applications such as phototherapy, gas sensing, plant growth lighting, and UV curing. In this paper we present high power UV-B LEDs grown by MOVPE on sapphire substrates. By optimizing the heterostructure design, growth parameters and processing technologies, significant progress was achieved with respect to internal efficiency, injection efficiency and light extraction. LED chips emitting at 310 nm with maximum output powers of up to 18 mW have been realized. Lifetime measurements show approximately 20% decrease in emission power after 1,000 operating hours at 100 mA and 5 mW output power and less than 30% after 3,500 hours of operation, thus indicating an L 50 lifetime beyond 10,000 hours.